On-line Utilities for SHARAKU
Polarized neutron reflectometer in MLF, J-PARC
Conversion between magnetic SLD and magnetic moment
Magnetic moment--->Magnetic Scattering Length Density SLDM
| material |
Magnetic moment μB |
Mass density[g/cm3] |
Atomic weight[g/mol] |
|
SLDM[10-4 nm-2] |
| Input here |
| Fe |
2.2 |
7.874 |
55.845 |
|
5.034 |
| Fe3Si |
1.65 |
7.214 |
195.620 |
|
9.875 |
| CoFe |
1.66 |
8.63 |
57.4 |
|
4.051 |
| NiFe |
0.92 |
8.63 |
57.3 |
|
2.249 |
Magnetic Scattering Length Density SLDM--->Magnetic moment
| material |
SLDM[10-4 nm-2] |
Mass density[g/cm3] |
Atomic weight[g/mol] |
|
Magnetic moment μB |
| Input here |
| Fe |
5.034 |
7.874 |
55.845 |
|
2.20 |
| Fe3Si |
9.875 |
7.214 |
195.620 |
|
1.65 |
| CoFe |
4.051 |
8.63 |
57.4 |
|
1.66 |
| NiFe |
2.249 |
8.63 |
57.3 |
|
0.92 |
Jump to Conversion between mass and atomic number densities
To Japanese.
Conversion between mass and atomic number densities
Number density of atoms,Atomic Number Density dens[atom/Å3]
| material |
Z (Z number) |
Vcell[Å] |
|
dens [atom/Å3] |
| Input here |
| Fe |
2 |
23.55 |
|
0.08492 |
| FeSi2 |
1 |
37.25 |
|
0.02685 |
| SiO2 |
3 |
92.90 |
|
0.03229 |
| EuS |
4 |
212.46 |
|
0.01883 |
| Si |
8 |
160.10 |
|
0.04997 |
dens [atom/Å3] --> Mass density[g/cm3]
| material |
dens [atom/Å3] |
Atomic weight[g/mol] |
|
Mass density[g/cm3] |
| Input here |
| Fe2O3 |
0.01976 |
159.69 |
|
5.24 |
| Fe |
0.08493 |
55.85 |
|
7.88 |
| FeSi2 |
0.02685 |
112.02 |
|
4.99 |
| SiO2 |
0.03229 |
60.08 |
|
3.22 |
| EuS |
0.01883 |
184.03 |
|
5.75 |
| Si |
0.04997 |
28.09 |
|
2.33 |
Jump to Conversion between magnetic SLD and magnetic moment
To Japanese.